Title Damage and dopant profiles produced by ultra-shallow boron and arsenic ion implants into silicon at different temperatures characterized by medium energy ion scattering
Abstract Medium energy ion scattering (MEIS), operated at sub-nm depth resolution in the double alignment configuration, has been used to examine implant and damage depth profiles formed in Si(100) substrates irradiated with 2.5 keV As+ and 1 keV B+ ions. Samples were implanted at temperatures varying between -150 °C, and 300 °C to doses ranging from 3 ´ 1014 to 2 ´ 1016 cm-2. For the As implants the MEIS studies demonstrate the occurrence of effects such as a dopant accommodation linked to the growth in depth of the damage, dopant clustering, as well as damage and dopant movement upon annealing. Following epitaxial regrowth at 600°C, approximately half of the As was observed to be in substitutional sites, consistent with the reported formation of AsnV complexes (n£4), while the remainder became segregated and became trapped within a narrow, 1.1 nm wide layer at the Si/oxide interface. MEIS measurements of the B implants indicate the formation of two distinct damage regions each with a different dependence on implant dose, the importance of dynamic annealing for implants at room temperature and above, and a competing point defect trapping effect at the Si/oxide interface. B+ implantation at low temperature resulted in the formation of an amorphous layer due to the drastic reduction of dynamic annealing processes. Notably different dopant distributions were measured by SIMS in the samples implanted with As at different temperatures following rapid thermal annealing (RTA) up to 1100 °C in an oxidising environment. Implant temperature dependent interactions between defects and dopants are reflected in the transient enhanced diffusion (TED) behaviour of As.
Organisation CCLRC , MEIS
Keywords Materials
Funding Information
Related Research Object(s):
Language English (EN)
Type Details URI(s) Local file(s) Year
Paper In Conference Proceedings SILICON FRONT-END JUNCTION FORMATION TECHNOLOGIES Book Series: MATERIALS RESEARCH SOCIETY SYMPOSIUM PROCEEDINGS Volume: 717 Pages: 303-308 Published: 2002 . Is in proceedings of: Symposium on Silicon Front-End Junction Formation Technologies held at the MRS Spring Meeting, San Francisco, CA., 2-4 Apr 2002. 2002
Showing record 1 of 1
Science and Technology Facilities Council Switchboard: 01793 442000