Title Dynamic Recrystallization and Dynamic Precipitation Behavior of a Fe-17Ni-0.2C Martensite Steel Studied by In Situ Neutron Diffraction
Abstract The austenite precipitation and dynamic recrystallization behaviors of 17Ni?0.2C martensite steel during isothermal tempering at 500°C followed by isothermal warm compression at 8.3 10 4/s were investigated in situ using neutron diffraction. The Rietveld analysis of Time-Of-Flight neutron diffraction profiles revealed that the austenite amount increased by about 1.5% during 10 min isothermal holding while the warm compression at 500°C accelerated the austenite precipitation. Splitting of the austenite (111) peak occurred and then disappeared during warm compression. Based on integrated intensities obtained by single peak fitting of neutron spectra, it was found from the axial neutron spectra that the ferrite (110) peak intensity rapidly decreased and the ferrite (200) and (211) peak intensities slowly increased during warm compression; the occurrence of dynamic recrystallization led to an evident deviation from this trend. The comparison between lattice strains and texture indexes of austenite and ferrite suggested that the austenite was harder than the ferrite at 500°C. Thus, heterogeneous deformation occurred in the ferrite, leading to accelerated dynamic recrystallization.
Organisation ISIS , ISIS-ENGIN-X , STFC
Keywords Engineering , neutron diffraction , warm deformation , dynamic recrystallization , dynamic precipitation , martensite , austenite , SSTD 2008-2009
Funding Information
Related Research Object(s):
Language English (EN)
Type Details URI(s) Local file(s) Year
Journal Article ISIJ International, 48, no. 11 (2008): 1618-1625. doi:10.2355/isijinternational.48.1618 Xu et al ISIJ Int (2008).pdf 2008
Showing record 1 of 1
Science and Technology Facilities Council Switchboard: 01793 442000